医疗级PBT，医疗/护理用品，无动物源性成分，ISO 10993，USP XXIII, Class VI，FDA食品级，DMF 10047，MAF 1078

Celanex® 2402 MT

聚丁烯对苯二甲酸酯

 

Celanese Corporation

 

Technical Data

 

Product Description

Celanex 2402MT is an unfilled and nucleated, easy flow PBT grade for injection molding processing.

Celanex 2402MT is a special grade developed for medical industry applications and complies with:

 

• CFR 21 (177.1660) of the Food and Drug Administration (FDA) and is listed in the Drug Master File (DMF 10047 (US) / 10033 (EU)) and the Device Master File (MAF 443 (US) / 1078 (EU)) 

• the corresponding EU and national registry regulatory requirements 

• biocompatibility in tests corresponding to USP 23 Class VI/ISO 10993 

• low residual monomers 

• no animal products 

 

General

Material Status • 已商用：当前有效

资料 1 • Technical Datasheet (English)

搜索 UL 黄卡 • Celanese Corporation

• Celanex®

Availability • 北美洲 • 拉丁美洲 • 亚太地区

• 非洲和中东 • 欧洲

Additive • 成核剂

Features • 成核的 • 良好的流动性 • 无动物源性成分

Uses • 医疗/护理用品

• DMF 10033 • ISO 10993 •

Agency Ratings • DMF 10047 • MAF 1078 USP XXIII, Class VI

• FDA 21 CFR 177.1660 • MAF 443

RoHS Compliance • 联系制造商

Processing Method • 注射成型

Physical 额定值(英制) 额定值(公制) 测试方法

Density 1.31g/cm³ 1.31g/cm³ ISO 1183

Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) 2.44in³/10min 40.0cm³/10min ISO 1133

Molding Shrinkage - 流量 1.8 到 2.2% 1.8 到 2.2% ISO 294-4

Mechanical 额定值(英制) 额定值(公制) 测试方法

Tensile Modulus 392000psi 2700MPa ISO 527-2/1A

Tensile Stress (屈服) 8700psi 60.0MPa ISO 527-2/1A/50

Tensile Strain (屈服) 4.0% 4.0% ISO 527-2/1A/50

Nominal Tensile Strain at Break 15% 15% ISO 527-2/1A/50

Flexural Modulus (73°F (23°C)) 370000psi 2550MPa ISO 178

Flexural Stress (73°F (23°C)) 11600psi 80.0MPa ISO 178

Impact 额定值(英制) 额定值(公制) 测试方法

Charpy Notched Impact Strength ISO 179/1eA

-22°F (-30°C) 2.1ft•lb/in² 4.5kJ/m²

73°F (23°C) 2.4ft•lb/in² 5.0kJ/m²

Charpy Unnotched Impact Strength ISO 179/1eU

-22°F (-30°C) 62ft•lb/in² 130kJ/m²

73°F (23°C) 64ft•lb/in² 140kJ/m²

Thermal 额定值(英制) 额定值(公制) 测试方法

Heat Deflection Temperature

66 psi (0.45 MPa), 未退火 320°F 160°C ISO 75-2/B

264 psi (1.8 MPa), 未退火 140°F 60.0°C ISO 75-2/A

Glass Transition Temperature 3 140°F 60.0°C ISO 11357-2

Vicat Softening Temperature 374°F 190°C ISO 306/B50

Melting Temperature 3 437°F 225°C ISO 11357-3

CLTE - 流动 6.1E-5in/in/°F 1.1E-4cm/cm/°C ISO 11359-2

 

Celanex® 2402 MT

聚丁烯对苯二甲酸酯

 

Celanese Corporation

Flammability 额定值 (英制) 额定值(公制) 测试方法

Flame Rating (0.031 in (0.8 mm)) HB HB UL 94

Injection 额定值(英制) 额定值(公制)

Drying Temperature 248 到 266°F 120 到 130°C

Drying Time 4.0hr 4.0hr

Suggested Max Moisture 0.020% 0.020%

Suggested Max Regrind 25% 25%

Hopper Temperature 68 到 122°F 20 到 50°C

Rear Temperature 446 到 464°F 230 到 240°C

Middle Temperature 455 到 482°F 235 到 250°C

Front Temperature 455 到 482°F 235 到 250°C

Nozzle Temperature 482 到 500°F 250 到 260°C

Processing (Melt) Temp 455 到 500°F 235 到 260°C

Mold Temperature 149 到 199°F 65 到 93°C

Injection Rate 中等偏快 中等偏快

Back Pressure 0.00 到 50.0psi 0.00 到 0.345MPa

Injection Notes

Die Temperature: 250 to 260°C

Feed Temperature: 230 to 240°C

Zone 4 Temperature: 240 to 260°C

 

 

 

 

ISO 10993医疗级聚丁烯对苯二甲酸酯,ISO 10993医疗级 PBT,PBT Celanex® 2402 MT是东莞市双帮塑胶原料有限公司常年销售的塑料，因为塑料价格行情每天都有新变化前天的报价不等于今天的报价。本公司销售的所有原料保证是原厂原包,随料可以提供生产厂商提供的物性表、SGS报告，COA原料出厂报告,REACH报告,SVHC报告,UL黄卡,提供原料注塑加工工程中可能出现的各种异常现象解决方法，塑料牌号太多，本网站没有提供的本公司也有代理，详情请咨询本公司相关业务人员0769-87795123   13549213581 肖生    QQ：15397858   微信：13549213581